High Speed Steels Sourced numerical data plus engineering analysis

Material / Grade

1.3343

HS6-5-2C

A widely used conventional high-speed steel associated with M2, combining wear resistance, toughness and red hardness for cutting tools.

Hardness potential98 / 100Comparison index

Toughness37 / 100Comparison index

Impact resistance29 / 100Comparison index

Bending resistance54 / 100Comparison index

Abrasive wear98 / 100Comparison index

Steel Overview

Complete introduction and metallurgical analysis

1.3343 / HS6-5-2C belongs to High Speed Steels and selection centres on red hardness, cutting-edge wear resistance and high compressive strength.

A widely used conventional high-speed steel associated with M2, combining wear resistance, toughness and red hardness for cutting tools.

The principal recorded elements are C≈0.9%, Cr≈4.1%, Mo≈5%, V≈1.8%, W≈6.2%. Mid-range values support engineering interpretation and do not replace purchase limits.

The expected microstructure is highly alloyed tempered martensite with a dense distribution of primary and secondary carbides; delivery condition, section size, melt quality and processing history can change that state.

Comparison indices are hardness 98/100, toughness 37/100, impact 29/100, wear 98/100 and bending 54/100. These are internal indices, not standard test results.

The screening temperature range is 450–600 °C; strength or hardness loss, oxidation, exposure time and creep must be assessed separately.

A representative process route is careful staged preheating, high-temperature hardening, rapid controlled cooling and multiple tempering. Obtain actual temperatures, times and cooling media from the grade and product data sheet.

Manufacturing indices are weldability 12/100, machinability 25/100, corrosion resistance 20/100 and fatigue resistance 49/100; use them for screening only.

The principal risk is grinding cracks, overheating, carbide segregation or brittle failure under shock loading. Evaluate geometry, surface condition, environment and the governing failure mechanism together.

A similar name or calculated relationship is not proof of interchangeability; match chemistry, specification, condition, heat treatment and MTC.

Engineering conclusion: 1.3343 / HS6-5-2C is a rational candidate when retention of cutting hardness at elevated edge temperatures matches the real load, environment and certified product condition.

Recorded standards:ISO 4957:2018

International Equivalents

International equivalents and designations

A close counterpart is not automatically interchangeable. Confirm chemistry, product standard, delivery condition, dimensions and heat treatment.

EN / DIN / ISOOfficial designation for the same grade

HS6-5-2C

A registered identity within the same grade record.

EN / W.NrOfficial designation for the same grade

1.3343

A registered identity within the same grade record.

W.NrOfficial designation for the same grade

1.3343

A registered identity within the same grade record.

PrimaryOfficial designation for the same grade

HS6-5-2C

A registered identity within the same grade record.

Chemical Composition

Chemical composition and the role of each element

The principal recorded elements are C≈0.9%, Cr≈4.1%, Mo≈5%, V≈1.8%, W≈6.2%. Mid-range values support engineering interpretation and do not replace purchase limits. Composition is shown for screening and traceability. The current purchase standard and the heat-specific MTC remain authoritative.

Element	Weight-percent range	Metallurgical role and effect
C	0.9–0.9 %	Carbon raises hardness, strength and carbide potential; excessive carbon can reduce toughness and weldability.
Cr	4.1–4.1 %	Chromium promotes hardenability and carbide formation and, at sufficient levels, corrosion or oxidation resistance.
Mo	5–5 %	Molybdenum improves hardenability and temper resistance and can support hot strength or pitting resistance.
V	1.8–1.8 %	Vanadium refines grain and forms stable carbides that support wear resistance and secondary hardening.
W	6.2–6.2 %	Tungsten forms hard carbides and supports hot hardness and abrasive-wear resistance in tool steels.

BÖHLER S600 — manufacturer average Sourced with conditions

Engineering Behaviour

Engineering behaviour and selection response

Hardness potential98 / 100

Hardenable; actual hardness depends on chemistry, section size, austenitizing, quench and tempering. Internal comparison index: 98/100.

Engineering analysis

Toughness37 / 100

Toughness has an internal index of 37/100 (low). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Impact resistance29 / 100

Impact resistance has an internal index of 29/100 (low). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Bending resistance54 / 100

Bending resistance has an internal index of 54/100 (moderate). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Abrasive wear98 / 100

Wear resistance depends on final hardness, microstructure and wear mode; grade name alone is insufficient for substitution. Internal comparison index: 98/100.

Engineering analysis

Corrosion resistance20 / 100

Corrosion performance depends on environment; chloride, temperature, pH and surface condition must be evaluated. Internal comparison index: 20/100.

Engineering analysis

Weldability12 / 100

Weldability has an internal index of 12/100 (very low). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Machinability25 / 100

Machinability has an internal index of 25/100 (low). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

High-temperature strength74 / 100

Temperature-dependent behavior varies with condition, exposure time, environment and product form; use sourced values for design. Internal comparison index: 74/100.

Engineering analysis

Creep resistance80 / 100

Creep resistance has an internal index of 80/100 (high). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Fatigue resistance49 / 100

Fatigue resistance has an internal index of 49/100 (moderate). Actual performance requires a documented product condition, heat treatment and test context.

Engineering analysis

Numerical scores are internal comparison indices. They are not standard test results, allowable design stresses or a manufacturer guarantee. Data Method

Hardness & Hardenability

Hardness and hardenability

Hardenable; actual hardness depends on chemistry, section size, austenitizing, quench and tempering. Internal screening index: 98/100 (very high).

98/100

very high

Comparison index

Governing factors

Chemistry and section size
Austenitising and quench severity
Tempering temperature and time
Test method and surface preparation

Data limits

Final acceptance requires the current standard, product form, dimensions, delivery condition and heat-specific MTC.

Impact & Toughness

Toughness, impact and fracture behaviour

Impact resistance is indexed at 29/100 and toughness at 37/100. These are not Charpy or Izod energy values; temperature, orientation, geometry and actual microstructure govern component behaviour.

29/100lowComparison index

Microstructure, hardness and grain size influence impact tolerance.
Sharp radii, notches and surface defects reduce fracture resistance.
Test temperature, specimen direction and section must be identified.
For critical parts, accept impact energy only from a documented test of the same condition.

Temperature & Creep

Service temperature, thermal stability and creep

Temperature-dependent behavior varies with condition, exposure time, environment and product form; use sourced values for design. 450–600 °C is a screening range or sourced limit according to its evidence label. Check strength loss, oxidation, creep, exposure time and environment.

Continuous service

450–600 °CEngineering guidance

Review the limit against strength or hardness loss and exposure time.

Intermittent service

Do not assign an intermittent limit without product-specific source data.

Tempering and phase stability

Working and coating temperatures must remain compatible with the tempering condition and required microstructure.

Oxidation and environment

Oxidation or corrosion may become limiting before the strength criterion.

Relative creep resistance80/100Comparison index

The relative creep index is 80/100 (high). It is not an allowable creep stress or rupture-life value.

Do not select this grade for long-term static high-temperature loading from the internal index alone.

Wear & Surface Behaviour

Wear resistance and surface behaviour

Abrasive wear

Wear resistance depends on final hardness, microstructure and wear mode; grade name alone is insufficient for substitution. The abrasive-wear index is 98/100; final hardness, carbides, microstructure, contact mode and lubrication govern actual resistance.

Comparison index

Adhesive wear

Assess adhesive wear with the counterface material, lubrication, roughness, pressure and temperature.

Engineering analysis

Surface improvement

Evaluate surface treatment or coating only after confirming compatibility with chemistry, substrate and process temperature.

Engineering guidance

Mechanical & Physical Properties

Mechanical and physical properties

The record contains 1 sourced mechanical-property rows; each applies only to its stated condition, dimensions and test temperature.

Property	Value	Condition	Dimension	Test temperature
Delivery hardness	≈ 250 HB	Annealed as cited	According to the product data sheet	According to the cited test

Sourced with conditions

Physical properties

Density, elastic modulus, expansion and conductivity depend on family, temperature and product condition. Use grade- and product-specific values for precise calculations.

Obtain density and expansion data from the product data sheet for dimensional calculations.
Elastic modulus and conductivity vary with temperature.

Engineering analysis

Heat Treatment

Heat-treatment stages and process controls

The representative family route is careful staged preheating, high-temperature hardening, rapid controlled cooling and multiple tempering. Numerical temperatures are shown only when supported by the record.

Annealing / stress relief

Engineering guidance

Assess the supply condition, residual stress, section size and prior machining before selecting time and temperature.

Cooling: Grade- and process-specific cooling

Preheating and austenitising

Engineering guidance

Set preheat steps and austenitising parameters from the grade/product data sheet and actual section size.

Cooling: Grade- and process-specific cooling

Quenching / controlled cooling

Engineering guidance

Choose the quench medium and cooling severity against hardenability, geometry, distortion and crack risk.

Cooling: Grade- and process-specific cooling

Tempering / property adjustment

Engineering guidance

Set tempering or ageing to the required hardness, toughness and service-temperature balance.

Cooling: Grade- and process-specific cooling

Tempering / property adjustment

Engineering guidance

Set tempering or ageing to the required hardness, toughness and service-temperature balance.

Cooling: Grade- and process-specific cooling

Process control: Review delivery condition, actual section, equipment capability, crack and distortion risk and target hardness before approving the cycle.

Engineering Charts

Hardness, toughness, impact, temperature and process charts

Chemistry data retain their evidence label; 0–100 charts are internal indices and stages without temperature are process sequences.

Multi-axis engineering profile

Comparison index

Chemical composition

Derived from source data

Hardness–toughness balance

Comparison index

Toughness, impact and fatigue

Comparison index

Wear and surface response

Comparison index

Mechanical properties or comparison indices

Sourced with conditions

Service temperature

Engineering guidance

Heat treatment

Engineering guidance

Related-grade similarity

Comparison index

All comparison indices

Comparison index

Failure Modes & Selection

Potential failure modes and selection guidance

Potential failure mechanisms

grinding cracks, overheating, carbide segregation or brittle failure under shock loading.
Fatigue initiation from surface defects, section transitions or stress concentration.
Property loss after unsuitable heat treatment, cooling or finishing.
Corrosion, oxidation or environmental attack when protection is inadequate.

Selection and design notes

Match designation, material number, product standard and supply form before purchase.
Compare the governing failure mechanism with hardness 98, toughness 37, impact 29 and wear 98 indices out of 100.
Use mechanical values only within their cited condition, dimensions and test temperature.
Confirm the heat-treatment route and target hardness with the processor before final machining.
Review the heat number, MTC and required test results before release.

Advantages & Limitations

Advantages, limitations and unsuitable applications

Advantages

retention of cutting hardness at elevated edge temperatures.
A clearly labelled engineering profile supports comparison with related grades.
Grade identity, chemistry, counterparts and references remain traceable in one dossier.

Limitations and weaknesses

grinding cracks, overheating, carbide segregation or brittle failure under shock loading.
A 0–100 index cannot be converted into design stress, impact energy or creep life.
Hardness and toughness depend on section, delivery condition and actual processing.
Do not approve a substitute before checking the product standard and heat-specific MTC.

Cases requiring caution or an alternative material

Critical design without condition- and section-specific test dataDirect substitution based only on name or similarity scoreLong-term creep service without sourced time–stress–temperature datagrinding cracks, overheating, carbide segregation or brittle failure under shock loading

Applications & Processing

Industrial applications and processing

Typical applications

Punches, dies and blanking tools
Industrial blades, knives and cutting tools
Drills, mills, taps, broaches and high-speed machining tools
drills, taps and milling cutters
broaches, reamers and hobs
high-speed cutting tools
wear-resistant tooling requiring hot hardness

Manufacture, welding and surface engineering

Weldability has an internal index of 12/100 (very low). Actual performance requires a documented product condition, heat treatment and test context.

Forming and forging depend on steel family, delivery condition and the grade-specific qualified temperature range.

Select nitriding, induction hardening or coating against chemistry, substrate hardness and application.
Keep coating-deposition temperature compatible with the tempering condition and substrate.
Control hydrogen embrittlement, residual stress and distortion in high-strength components.

Engineering Conclusion

Engineering conclusion and selection recommendation

1.3343 / HS6-5-2C is worth evaluating when the principal need is retention of cutting hardness at elevated edge temperatures. Internal indices of hardness 98/100, toughness 37/100, impact 29/100 and wear 98/100 must be aligned with the real failure mechanism. The leading risk is grinding cracks, overheating, carbide segregation or brittle failure under shock loading. Final approval requires the current standard, product form, dimensions, delivery condition, heat treatment and heat-specific MTC.

Engineering analysis

Shaygan Steel — the right choice in alloy steel

Compare with other steels View similar steels

Frequently Asked Questions

Frequently asked questions

What is 1.3343 / HS6-5-2C steel?

A widely used conventional high-speed steel associated with M2, combining wear resistance, toughness and red hardness for cutting tools.

What are the main applications of 1.3343 / HS6-5-2C?

Application contexts include Punches, dies and blanking tools, Industrial blades, knives and cutting tools, Drills, mills, taps, broaches and high-speed machining tools and drills, taps and milling cutters, subject to the product standard and actual condition.

How hard can 1.3343 / HS6-5-2C be?

Hardenable; actual hardness depends on chemistry, section size, austenitizing, quench and tempering. Internal screening index: 98/100 (very high).

Is 1.3343 / HS6-5-2C suitable for impact loading?

Impact resistance is indexed at 29/100 and toughness at 37/100. These are not Charpy or Izod energy values; temperature, orientation, geometry and actual microstructure govern component behaviour.

What is the service-temperature limit of 1.3343 / HS6-5-2C?

Can 1.3343 / HS6-5-2C be replaced by a close grade?

Approve substitution only after matching chemistry, specification, product form, condition, heat treatment and MTC.

Steel Comparison

Engineering steel comparison

Compare this grade with any other dossier. Scores from 0 to 100 are internal screening indices, not laboratory values or allowable design stresses.

Close suggestions:

Search for the second steel

Current grade1.3343 / HS6-5-2CHigh Speed Steels

Selected grade1.3243 / BÖHLER S705High Speed Steels

Current-grade chemistry

Second-grade chemistry

Current-grade heat treatment

Second-grade heat treatment

Current-grade applications

Limitations

Second-grade applications

Limitations

Select a second grade to update the comparison.

Sources & Evidence

Sources, methodology and evidence

Sources support grade identity, recorded values or the engineering method. General guidance does not replace product-specific certification.

Grade-specific sources

BÖHLER S600 — 1.3343 / HS6-5-2CManufacturer data sheet · Tier A

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: manufacturer datasheet.

View source

E M2 high speed steel user guideManufacturer data sheet · Tier A

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: manufacturer datasheet.

View source

BÖHLER S500 — 1.3247 / HS2-9-1-8Manufacturer data sheet · Tier A

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: manufacturer datasheet.

View source

E M42 / high-speed steel grade summaryManufacturer catalog · Tier A

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: manufacturer catalog.

View source

steelnumber.comDesignation cross-reference · Tier B

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: identity crosswalk.

View source

stahldaten.deOfficial material-number register · Tier A

Reference supporting grade identity or recorded values; interpret it within the cited product and condition context. Role: official material number register.

View source